Influence of Initial Fibre Length and Content Used in the Injection Moulding of CFRP on the Properties of C/C and C/C-SiC Composites

The production of C/C-SiC composites comprises a three-stage process: forming (CFRP-composite), pyrolysis (C/C-composite) and liquid silicon infiltration (C/C-SiC). A new promising approach for the manufacturing of CFRP intermediate composites is the injection moulding of customised granulates (novolac resin, hardener, processing additives and short carbon fibre) produced by compounding technique. To date, a direct dosing of short carbon fibre into the compounder was technically not realisable due to fibre separation and electrostatic charging in the hopper. A possible substitute solution has been the direct feeding of a carbon fibre bundle from a roving into the compounder. However, this is associated with a severe damage of the fibres and an inaccurate adjustment of the fibres content. In the present article, new chopped carbon fibres provided with an adapted sizing to be directly dosed into the compounder are used. The fibres possess a predefined length of 3 and 6 mm and their content amounts to 50 and 58 wt.%. The influence of the initial fibre length and fibre content on the physical and mechanical properties of the resulting CFRP-, C/C-and C/C-SiC-composites is presented and discussed. In addition, the impact of fibre feeding procedure at the compounding stage on the microstructure is considered