Magnetic and Dielectric Properties of 0.1 Bi2/3Cu3Ti4O12 -0.9 Bi3LaTi3O12 Nanocomposite Prepared by Semi-Wet Route

INTRODUCTION: A chemical formula of nanocomposite 0.1 Bi2/3Cu3Ti4O12 -0.9 Bi3LaTi3O12 (BCLT-19) was prepared by semiwet route using metal nitrate and solid TiO2. The phase formation of Bi2/3Cu3Ti4O12 (BCT) and Bi3LaTi3O12 (BLT) was confirmed by X-ray diffraction (XRD) study. METHOD: Transmission electron microscope (TEM) analysis showed a nano particle of size 14 ± 5 nm on average for BCLT-19 composites. Scanning electron microscope (SEM) images exhibited a tubular, spherical and heterogeneous structure of grains. The root means square roughness, average roughness and maximum area peak height were explained by atomic force microscopy (AFM). RESULT: Study of magnetic properties was determined as weak antiferromagnetic to ferromagnetic and in nature. The high dielectric constant (ε' = 3147 at 100Hz to 500 K) of BCLT-19 may be due to the existence of space charge polarization. CONCLUSION: In this manuscript have studies on the novel composite materials of BCLT-19 micro-structural properties. This is useful for future Random-access memory devices and dielectric materials,