DIMENSIONAL CHANGE OF UHMWPE AFTER AGING

IntroductionMechanical properties of irradiated Ultra High Molecular Weight Polyethylene (UHMWPE) after aging have been well documented. However there was no sufficient data for the dimensional change due to irradiation and aging. This change may have adverse effects to the implant modular locking mechanism. The purpose of this study was to characterize the dimensional change of UHMWPE after irradiation and aging.Materials and MethodTotal (30) o15mm × 50mm virgin GUR 1050 UHMWPE rods were cleaned, dried, inspected, vacuum packaged and stored in 20°C environment for 2 days. Among them, (20) samples were measured along the 50mm length at 20°C +/-2°C before and after two conditions: 1, (10) were submerged in 40°C DI water for 2 hours and dried in 40°C to simulate the cleaning process and 2, (10) were soaked in 37°C saline for 14 days to simulate initial in-vivo environment. Remaining (10) samples were measured in the same way after irradiation of 30KGy dosage and then measured again after soaking in 37°C sal...