Morphology and microstructure of hydrating Portland cement and its constituents IV. Changes in hydration of A C3S, C3S, C3A, C4AF and gypsum paste with and without the admixtures triethanolamine and calcium lignosulphonate

Systematic sequential observations with the electron microscope were made of morphological changes which occurred during hydration of a paste mixture of C3S, C2S, C3A, C4AF and gypsum. The pronounced effect on rate of hydration of each of two organic admixtures was clearly observed. Differences could be seen also in the stability and habit of hydration products and in the microstructure itself. The electron micrographs shown illustrate the forms of the products at different hydration times. Des observations au microscope électronique ont été faites en séquence systématique pour observer les changements morphologiques qui prenaient place au cours de l'hydratation d'une pâte de C3S, C2S, C3A, C4AF et de gypse. Les effets prononcés de deux adjuvants organiques sur la vitesse d'hydratation ont été nettement observés. On a pu constater des différences dans la stabilité et l'habitus des produits d'hydratation de même que dans la microstructure elle-même. Les résultats de la micrographie qui sont présentés illustrent la forme des produits à différents stages de l'hydratation.