Zhiwei Qu,Zihao Liu,Ruizhe Si,Yingda Zhang
出处
期刊:Materials
[Multidisciplinary Digital Publishing Institute]
日期:2022-04-21
卷期号:15 (9): 3016-3016
被引量:19
摘要
Concrete is known as the most globally used construction material, but it releases a huge amount of greenhouse gases due to cement production. Recently, Supplementary Cementitious Materials (SCMs) such as fly ash and Ground Granulated Blast Furnace Slag (GGBFS) have been widely used in concrete to reduce the cement content. However, SCMs can alter the mechanical properties and time-dependent behaviors of concrete and the early age mechanical properties of concrete significantly affect the concrete cracking in the engineering field. Therefore, evaluation of the development of the mechanical properties of SCMs-based concrete is vital. In this paper, the time development of mechanical properties of concrete mixes with various fly ash and GGBFS was experimentally investigated. Four different cement replacement levels including 0%, 20%, 30%, and 40% by fly ash and GGBFS as well as ternary binders were considered. Compressive strength, splitting tensile strength, flexural strength, and elastic modulus of concrete were measured until 28 days. Three additional concrete mixes with ternary binders were also cast to investigate the early-age autogenous shrinkage development until 28 days. In addition, prediction models in existing standards were used and compared to experimental results. The comparison results showed that the prediction models overestimated the compressive strength but underestimated the splitting tensile strength development and autogenous shrinkage. As a result, a model capturing the effect of fly ash and GGBFS on the development of compressive and splitting tensile strength is proposed to improve the prediction accuracy for current standards and empirical models.
科研通智能强力驱动
Strongly Powered by AbleSci AI