CrAlSiN nanocomposite thin films for high-speed machining applications

CrAlSiN nanocomposite thin films with varying film chemistry were developed on tungsten carbide (WC) specimens using cylindrical cathodic arc physical vapor deposition (c-CAPVD) technique. The physical, mechanical, and tribological properties of all the films were comprehensively investigated for arriving at the film chemistry leading to the best properties with respect to mechanical applications. The best tribo-mechanical properties were obtained in films with Cr/(Al+Si) ratio of 1.2. This coating with best properties was translated on to WC drill bits for machining tests. The Al and Si content has shown major influence on the adhesion strength and phase constitution of the films, with a considerable change in residual stress too. The superior properties achieved could be attributed to the formation of a near-perfect nanocomposite structure, with the crystalline CrAlN phase surrounded by an amorphous Si3N4 phase. The tool life of the coated CrAlSiN tools was investigated during dry machining of EN 24 material. In comparison to the tool life of an uncoated tool and a TiAlSiN-coated tool, the best CrAlSiN coatings synthesized in this study performed exceedingly well. The present study clearly demonstrates the advantages of CrAlSiN over other existing similar coatings for high-speed machining.