A Passive-Active Anti/Deicing Coating Integrating Superhydrophobicity, Thermal Insulation, and Photo/Electrothermal Conversion Effects

Anti/deicing coatings that combine active and passive methods can utilize various energy sources to achieve anti/deicing effects. However, poor photothermal or electrothermal performance and inevitable heat loss often reduce their anti/deicing efficiency. Herein, copper sulfide loaded activated biochar (AC@CuS) as photo/electric material, polydimethylsiloxane as hydrophobic component, thermally expandable microspheres as foaming agent, and an anti/deicing coating integrating thermal insulation, superhydrophobicity, photo/electrothermal effects was successfully constructed. Benefiting from the synergistic effect of superhydrophobicity and thermal insulation, the freezing time of water droplets on the coating surface is extended from 150 to 2140 s, showing excellent passive anti-icing performance. AC@CuS exhibits photo/electrothermal effects, and porous expanded microspheres reduce heat loss, which endows the coating with desirable photo/electrothermal conversion performance. Under the conditions of 0.2 W/cm2 electric power density (EPD) and 0.1 W/cm2 optical power density (OPD), the temperature of the coating increases from 24 to 96.4 and 113 °C, respectively. Interestingly, with a coheating of 0.05 W/cm2 weaker OPD and 0.05 W/cm2 lower EPD, the ice on the coating surface can be quickly melted in 2.5 min, showing synergistic deicing performance. In addition, the WCA of the prepared coating remains above 150° after mechanical damage, rain impact, UV irradiation, chemical corrosion, and high-temperature treatment, and good superhydrophobic durability ensures the anti/deicing durability of the coating.