Microstructure and properties of in situ TiC-reinforced Ti750 composite prepared by SPS

Purpose Titanium alloys and composites have proven to contain desirable properties for use at elevated temperatures. One such material is the Ti750 composite, which can be used at temperatures up to 750°C for a brief period. This paper aims the microstructure, phase compositions, apparent porosity and hardness of both sintered and heat-treated TiC reinforced Ti750 composites for consideration in aircraft engine design. Design/methodology/approach The fabrication of TiC-reinforced Ti750 composites was achieved through spark plasma sintering (SPS). To analyze the microstructure and X-ray diffraction, a scanning electron microscope (SEM) with model number S-3400N and a D8 advance model machine were used, respectively. The microhardness of the samples was measured using a Vickers hardness tester with model HV-1000. The research incorporated three solid solution treatments: 975°C/3 h/AC, 1,010°C/3 h/AC and 1,025°C/3 h/AC, along with a solid-solution aging treatment at 1,010°C/3 h/AC + 750°C/8 h/AC. Additionally, oxidation analysis was conducted on the samples. Findings The microstructures contained enhanced TiC and Ti5Si3 phases in the near a-Ti matrix. The microhardness of the sintered composite was over twice that of the matrix alloy, and its porosity was reduced by about 0.35%. The sample treated at 1,010°C/3 h/AC had the highest enhanced peaks and microhardness of 1,277.1 HV. After oxidation at 800°C for 100 h, the accumulated weight of the solid solution composite at 1,010 °C/3 h/AC was the lowest (3.0 mg.cm -2 ). The surface microstructure contained oxides of TiO2 and a spalling white area containing a small amount of Al 2 O 3 and SiO 2 . Originality/value There is limited research on Ti-Al-Sn-Zr-Mo-Si-based TMCs using a combination of the SPS method. This study used SiCp as a reinforcement for the Ti750 matrix alloy. The consolidation of SiCp and Ti750 powders using the SPS method, heat treatment of the resulting TiC reinforced Ti750 composites and study of the microstructure and properties of the composites are not found in literature or under consideration for publication in any media.