Effect of Annealing Process on Microstructure and Tensile Properties of TC16 Titanium Alloy after Rapid Heat Treatment

TC16 titanium alloy is a martensite α+β two-phase high strength titanium alloy, which can improve its structure and enhance properties through heat treatment. Effect of annealing process on microstructure and tensile properties of TC16 titanium alloy was investigated using optical microscope, scanning electron microscope and universe tensile test machine. The results show that when annealed at 720°C for 4h then furnace cooling to ambient temperature, the tensile strength of the TC16 alloy reaches nearly 900MPa,the elongation reaches 19.6% and the reduction of area reaches 65%, which present a good comprehensive performance.