The wetting behaviors of Al-Si-Cu-Mg-Zn brazing materials on 5083 aluminum alloy substrate were investigated through changing the proportion of Mg from 0 to 2 wt.%. The experimental results showed that the welding process goes through the three following stages: slow spreading, fast spreading, and stabilizing. The wettability of the brazing material was improved effectively, and the porosity of the interfacial layer was reduced, with the addition of Mg. With Mg content at 1 wt.%, the wetting diameter reached a maximum value of 20.46 mm. The reaction mechanism of the wetted interfacial layer between the brazing material and substrate alloy was illustrated with dynamic data, provided through experimentation and simulated thermodynamic calculation, and showed that the wetting behavior of the resultant Al-7.5Si-15Cu-1Mg-5Zn brazing material was dominated primarily by a diffusion reaction from elemental magnesium.