Understanding radiation effects in friction stir welded MA956 using ion irradiation and a rate theory model

材料科学 焊接 微观结构 肿胀 的 辐照 复合材料 空隙(复合材料) 成核 透射电子显微镜 冶金 化学 纳米技术 物理 有机化学 核物理学
作者
E. Getto,Nadia Nathan,J McMahan,Stephen Taller,Bill J. Baker
出处
期刊:Journal of Nuclear Materials [Elsevier BV]
卷期号:561: 153530-153530 被引量:3
标识
DOI:10.1016/j.jnucmat.2022.153530
摘要

• Coarsening of welded dispersoids noted at higher irradiation temperatures. • Any amount of welding increased void swelling, with maximum swelling of 0.5%. • The dislocation behavior was inconsistent between base material and welded sample. An outstanding challenge in the manufacturing and joining of oxide dispersion strengthened steels is retaining the nanofeatures in the alloy throughout the fabrication and welding process. MA956 was friction stir welded with two different sets of welding parameters, resulting in a medium and high heat input. After welding, 5 MeV Fe ++ ion irradiations were performed at doses ranging from 50 to 200 dpa in the temperature range of 400 to 500 °C. Post-irradiation characterization was performed with scanning transmission electron microscopy and energy-dispersive x-ray spectroscopy to investigate the Y-Al-O dispersoids, voids, and dislocations. After welding, the dispersoid microstructure coarsened, resulting in fewer and larger dispersoids regardless of heat input. After irradiation, the dispersoid behavior in the welded material was sensitive to temperature, exhibiting growth behavior attributed to Ostwald coarsening at 500 °C but a mixture of nucleation and more muted growth at 400 and 450 °C, attributed to competing mechanisms of radiation-enhanced diffusion and Ostwald coarsening. Void swelling correlated to heat input; being more prevalent in the welded conditions occurring at lower doses and in higher values relative to the base material. The low values of swelling despite microstructure coarsening caused by welding demonstrate the excellent swelling resistance of MA956, even after welding with the highest swelling values of 0.5% noted in the stir zone high heat input condition at 450 °C, 200 dpa. The dislocation behavior was inconsistent: the strongest trend was that network density was higher for welded versus base material, and an increase in loop diameter with temperature was observed. A rate theory model based on the observed microstructure suggests at high temperature interstitial loss to sinks was more likely to be dominant compared to mutual annihilation via point defect recombination, because of an increase of the radiation diffusion coefficient with temperature regardless of initial welded microstructure.
最长约 10秒,即可获得该文献文件

科研通智能强力驱动
Strongly Powered by AbleSci AI
更新
PDF的下载单位、IP信息已删除 (2025-6-4)

科研通是完全免费的文献互助平台,具备全网最快的应助速度,最高的求助完成率。 对每一个文献求助,科研通都将尽心尽力,给求助人一个满意的交代。
实时播报
懒癌晚期完成签到,获得积分10
1秒前
张csc完成签到 ,获得积分10
4秒前
一枝完成签到 ,获得积分10
4秒前
梦XING完成签到 ,获得积分10
5秒前
舒适映寒完成签到,获得积分10
6秒前
幽默梦之完成签到 ,获得积分10
6秒前
欢喜的凡之完成签到 ,获得积分10
10秒前
碎冰蓝完成签到,获得积分10
14秒前
怕孤独的香菇完成签到 ,获得积分10
16秒前
hcdb完成签到,获得积分10
16秒前
yk完成签到 ,获得积分10
17秒前
我爱康康文献完成签到 ,获得积分10
18秒前
18秒前
叶远望完成签到 ,获得积分10
19秒前
Jeffery426完成签到,获得积分10
28秒前
貔貅完成签到,获得积分10
30秒前
33秒前
太叔夜南完成签到,获得积分10
34秒前
小李新人完成签到 ,获得积分10
35秒前
35秒前
啦啦啦完成签到 ,获得积分10
36秒前
tangyangzju发布了新的文献求助10
40秒前
白小橘完成签到 ,获得积分10
47秒前
tangyangzju完成签到,获得积分10
47秒前
带志完成签到 ,获得积分10
47秒前
juan完成签到 ,获得积分10
48秒前
嘟嘟完成签到 ,获得积分10
51秒前
吱吱完成签到 ,获得积分10
51秒前
52秒前
呆萌的小海豚完成签到,获得积分10
54秒前
优雅莞完成签到,获得积分10
55秒前
Lamis完成签到 ,获得积分10
57秒前
直率的菠萝完成签到 ,获得积分10
1分钟前
zshhay完成签到 ,获得积分10
1分钟前
高是个科研狗完成签到 ,获得积分10
1分钟前
aiyawy完成签到 ,获得积分10
1分钟前
yshj完成签到 ,获得积分10
1分钟前
able完成签到 ,获得积分10
1分钟前
1分钟前
Echo_1995发布了新的文献求助10
1分钟前
高分求助中
A new approach to the extrapolation of accelerated life test data 1000
Cognitive Neuroscience: The Biology of the Mind 1000
Technical Brochure TB 814: LPIT applications in HV gas insulated switchgear 1000
Immigrant Incorporation in East Asian Democracies 600
Nucleophilic substitution in azasydnone-modified dinitroanisoles 500
不知道标题是什么 500
A Preliminary Study on Correlation Between Independent Components of Facial Thermal Images and Subjective Assessment of Chronic Stress 500
热门求助领域 (近24小时)
化学 材料科学 医学 生物 工程类 有机化学 生物化学 物理 内科学 纳米技术 计算机科学 化学工程 复合材料 遗传学 基因 物理化学 催化作用 冶金 细胞生物学 免疫学
热门帖子
关注 科研通微信公众号,转发送积分 3968559
求助须知:如何正确求助?哪些是违规求助? 3513391
关于积分的说明 11167370
捐赠科研通 3248808
什么是DOI,文献DOI怎么找? 1794465
邀请新用户注册赠送积分活动 875116
科研通“疑难数据库(出版商)”最低求助积分说明 804664