Effect of oxygen vacancies and phases on catalytic properties of hydrogen-treated nanoceria particles

Nanoceria powder was treated by hydrogen or air at different temperatures and atmospheres, and the phases, oxygen vacancies, catalytic properties of the treated samples were investigated. After treating, the crystallites on the ceria surface were fused, and the SEM and TEM images indicated that the particle size increased with treatment temperature. Both Raman and XPS spectra showed the oxygen vacancies in nanoceria increased with treatment temperature in hydrogen, and at the same temperature CeO2 treated in hydrogen had a higher Ce3+ fraction than that treated in air. The nanoceria after being treated in hydrogen at 900 °C contained the Ce2O3 phase together with CeO2 which was revealed by XRD and TEM results. Oxygen vacancies were found to enhance CO conversion, but the high temperature needed to generate the oxygen vacancies caused the fusion of the crystallites on the ceria surface and thus its area decreased, which resulted in lower catalytic activity. The catalytic activity of nanoceria treated in hydrogen at 900 °C measured higher than that of the ceria powders treated at 700 °C in hydrogen or 900 °C in air, which indicated that the Ce2O3 phase present in the treated nanoceria particles enhanced the catalytic activity.