Synthesis and electrochemical performances of core-shell structured Li[(Ni1/3Co1/3Mn1/3)0.8(Ni1/2Mn1/2)0.2]O2 cathode material for lithium ion batteries

Micro-scale core-shell structured Li[(Ni1/3Co1/3Mn1/3)0.8(Ni1/2Mn1/2)0.2]O2 powders for use as cathode material are synthesized by a co-precipitation method. To protect the core material Li[Ni1/3Co1/3Mn1/3]O2 from structural instability at high voltage, a Li[Ni1/2Mn1/2]O2 shell, which provides structural and thermal stability, is used to encapsulate the core. A mixture of the prepared core-shell precursor and lithium hydroxide is calcined at 770 °C for 12 h in air. X-ray diffraction studies reveal that the prepared material has a typical layered structure with an R3¯m space group. Spherical morphologies with mono-dispersed powders are observed in the cross-sectional images obtained by scanning electron microscopy. The core-shell Li[(Ni1/3Co1/3Mn1/3)0.8(Ni1/2Mn1/2)0.2]O2 electrode has an excellent capacity retention at 30 °C, maintaining 99% of its initial discharge capacity after 100 cycles in the voltage range of 3–4.5 V. Furthermore, the thermal stability of the core-shell material in the highly delithiated state is improved compared to that of the core material. The resulting exothermic onset temperature appear at approximately 272 °C, which is higher than that of the highly delithiated Li[Ni1/3Co1/3Mn1/3]O2 (261 °C).