Thermodynamic properties of the double oxides of Na2O with the oxides of Cr, Ni and Fe

EMF data obtained from cells with solid electrolytes and literature data were combined to obtain the following free energy relations for the temperature range 700–1100 K: ΔG°(NaCrO2) = (−208.9 + 49.97 × 10−3 T) ± 2.0 kcal mol−1; ΔG° (Na2FeO2) = (−185.6 + 49.67 × 10−3T) ± 5.0 kcal mol−1; ΔG° (NaFeO2) = (−167.6 + 45.25 × 10−3 T) ± 5.0 kcal mol−1; ΔG°(Na4FeO3) = (−290.4 + 81.85 × 10−3 T) ± 3.0 kcal mol−1. These data and literature data were employed to explain the observed corrosion behavior of Fe-Cr-Ni alloys exposed to oxygen containing sodium. Les données de force électromotrice obtenues à partir de cellules à electrolyte solide et de données de la littérature ont été combinées afin d'obtenir les relations suivantes d'énergie libre en fonction de la température, dans l'intervalle 700–1100 K: ΔG°(NaCrO2) = (−208,9 + 49,97 × 10−3 T) ± 2,0 kcal mol−1; ΔG° (Na2FeO2) = (−185,6 + 49,67 × 10−3 T) ± 5,0 kcal mol−1; ΔG° (NaFeO2) = (−167,6 + 45,25 × 10−3 T) ± 5,0 kcal mol−1; ΔG°(Na4FeO3) = (−290,4 + 81,85 × 10−3 T) ± 3,0 kcal mol−1. Ces données et celles de la littérature ont été utilisées pour expliquer les observations du comportement à la corrosion des alliages Fe-Cr-Ni exposés à du sodium contenant de l'oxygène. EMK-Ergebnisse aus Ketten mit Festelektrolyten ergeben zusammen mit Literaturdaten folgende Beziehungen für die freie Bildungsenthalpie zwischen 700 und 1100 K: ΔG°(NaCrO2) = (−208,9 + 49,97 · 10−3 T) ± 2,0 kcal/mol; ΔG° (Na2FeO2) = (−185,6 + 49,67 · 10−3 T) ± 5,0 kcal/mol; ΔG° (NaFeO2) = (−167,6 + 45,25 · 10−3 T) ± 5,0 kcal/ mol; ΔG°(Na4FeO3) = (−290,4 + 81,85 · 10−3 T) ± 3,0 kcal/mol. Diese und Literaturdaten werden zur Erklärung des beobachteten Korrosionsverhaltens von Fe-Cr-Ni-Legierungen, die sauerstoffhaltigem Natrium ausgesetzt sind, verwendet.