Correlating the morphological changes to electrochemical performance during carbon corrosion in polymer electrolyte fuel cells

Carbon corrosion in catalyst layer of PEFCs showed two phases: in first 500 AST cycles carbon corroded rapidly and catalyst layer thickness was lost, after that corrosion slowed down but a pore structure collapsed, increasing O 2 transport resistance.