Poly(n-vinylpyrrolidone) hydrogels: 2.Hydrogel composites as wound dressing for tropical environment

POLY(N-VINYLPYRROLIDONE) HYDROGELS: 2. HYDROGEL COMPOSITES AS WOUND DRESSING FOR TROPICAL ENVIRONMENT. The effects of irradiation on hydration and other properties of poly(vinylpyrrolidone) (PVP) hydrogel composites have been investigated. The aqueous solution of vinylpyrrolidone (VP) 10 wt % was mixed with several additives such as agar and polyethylen glycol (PEG). The solution was then irradiated with gamma rays from Cobalt-60 source at room temperature. Several parameters such as elongation at break (EB), tensile strength (TS), degree of swelling (DS), water vapor transmission rate (WVTR), equilibrium water content (EWC), microbial growth and penetration test, and water activity (Aw) were analysed at room temperature of 29 ±2°C humidity of 80 ± 10%. Results show that elongation at break of hydrogel membranes with initial composition of VP with agar, VP with agar and PEG were 240 % and 250 % kGy, the equilibrium water content of membranes were 96 to 90%, whereas degree of swelling were 55 to 10. The WVTR of hydrogel membranes with initial composition of VP with agar and PEG was 70 g m-2h-1, while the water activity was 0.9. Such hydrogel membranes exhibits the following properties: They are elastic, transparent, flexible, impermeable for bacteria. They absopt a high capacity of water, attached to healthy skin but not to the wound and they are easy to remove. These properties of the hydrogel membranes allow for applying as a wound dressings in tropical environment.