Assessing of cesium removal from wastewater using functionalized wood cellulosic adsorbent

Sustainable materials are urgently desired for treatment of radioactive cesium (Cs) contaminated water to safe-guard the public health. Apart from the synthetic ligand-based materials, the Mangrove charcoal modified adsorbent was fabricated for assessing of Cs removal from waste sample. The raw charcoal was oxidized using nitrification approach and diverse oxygen containing carboxyl, carbonyl and hydroxyl functional groups were introduced. After modification, the adsorbent characteristics were drastically changed as compared to the charcoal during the measurement of FTIR, N 2 adsorption-desorption isotherms and SEM micrographs. The data clarified that charcoal modified adsorbent was exhibited high Cs transport through the inner surface of the adsorbent based on bonding ability. The adsorbent was shown comparatively slow kinetics to Cs ion; however, the adsorption capacity was high as 133.54 mg/g, which was higher than the crown ether based conjugate materials. The adsorption data were followed to the Langmuir adsorption isotherms and the monolayer coverage was possible due to the data presentation. The presence of high amount of Na and K were slightly interfered to the Cs adsorption by the charcoal modified adsorbent, however; the Na and K concentration was 350–600 folds higher than the Cs concentration. Then the proposed adsorbent was selective to Cs for the potential real radioactive Cs contaminated water. The volume reduction was established rather than desorption and reuses advantages. More than 99% volume reduction was measured by burning of Cs adsorbed adsorbent at 500 °C for ensuring the safe storage and disposal of used adsorbent. Therefore, the charcoal modified adsorbent may open the new door to treat the Cs containing wastewater. • A cellulosic charcoal modified adsorbent was fabricated for cesium (Cs) removal. • The adsorbent was selectively taken up Cs even in the presence of high-level Na & K. • The Cs adsorption was high as enormous functional groups as expected in adsorbent. • Volume reduction was established rather than desorption and reuses advantages.